Investigation of the Effects of Heat Treatment Applied to Beech Plywood


Creative Commons License

Lunguleasa A., AYRILMIŞ N. , Spirchez C., ÖZDEMİR F.

DRVNA INDUSTRIJA, cilt.69, sa.4, ss.349-355, 2018 (SCI İndekslerine Giren Dergi) identifier identifier

  • Cilt numarası: 69 Konu: 4
  • Basım Tarihi: 2018
  • Doi Numarası: 10.5552/drind.2018.1768
  • Dergi Adı: DRVNA INDUSTRIJA
  • Sayfa Sayıları: ss.349-355

Özet

The aim of this study is to determine the effects of heat treatment on some physical and mechanical properties of beech plywood boards. The 3-layered beech plywood boards with a thickness of 3.9 mm were subjected to heat treatment for 1, 2 and 3 hours at temperatures of 160, 180 and 200 degrees C. These beech plywood boards were tested for physical properties such as density, water absorption and thickness swelling, mechanical properly tests such as modulus of rupture (MOR) and Brinell hardness, and mass loss rates according to the relevant standards. The results obtained show that the hydrophobicity of beech plywood boards is improved but the strength and weight loss are adversely affected, depending on the temperature and duration of heat treatment. It has been found that beech plywood boards heat-treated at 200 degrees C for 3 hours can be used in very humid environments for average mechanical stresses of wood parts with a reduced thickness swell of 4 % and a reduced water absorption rate of more than 12 %.