Properties of Flat-Pressed Wood Plastic Composites Containing Fire Retardants


Creative Commons License

Ayrilmis N. , BENTHIEN J. T. , THOEMEN H., White R. H.

JOURNAL OF APPLIED POLYMER SCIENCE, cilt.122, ss.3201-3210, 2011 (SCI İndekslerine Giren Dergi)

  • Cilt numarası: 122 Konu: 5
  • Basım Tarihi: 2011
  • Doi Numarası: 10.1002/app.34346
  • Dergi Adı: JOURNAL OF APPLIED POLYMER SCIENCE
  • Sayfa Sayısı: ss.3201-3210

Özet

This study investigated physical, mechanical, and fire properties of the flat-pressed wood plastic composites (WPCs) incorporated with various fire retardants (FRs) [5 or 15% by weight (wt)] at 50 wt % of the wood flour (WF). The WPC panels were made from dry-blended WF, polypropylene (PP) with maleic anhydride-grafted PP (2 wt %), and FR powder formulations using a conventional flat-pressing process under laboratory conditions. The water resistance and strength values of the WPC panels were negatively affected by increasing the FR content as compared to the WPC panels without FR. The WPC panels incorporated with zinc borate (ZB) gave an overall best performance in both water resistance and strength values followed by the panels containing magnesium hydroxide (MH) and ammonium polyphosphate (APP). For these three FR's, the best fire resistance as measured in the cone calorimeter was obtained with the 15 wt % APP treatment and then followed by 15 wt % ZB, or 15 wt % MH formulations. (C) 2011 Wiley Periodicals, Inc. J Appl Polym Sci 122: 3201-3210, 2011