Effects of chrome oxide and limestone filler on the wear characteristics of paste and concretes made with white Portland cement


Colak A.

CONSTRUCTION AND BUILDING MATERIALS, cilt.22, ss.2276-2280, 2008 (SCI İndekslerine Giren Dergi)

  • Cilt numarası: 22 Konu: 11
  • Basım Tarihi: 2008
  • Doi Numarası: 10.1016/j.conbuildmat.2007.08.007
  • Dergi Adı: CONSTRUCTION AND BUILDING MATERIALS
  • Sayfa Sayısı: ss.2276-2280

Özet

This paper is concerned with the wear characteristics of limestone filler blended white Portland cement paste and concretes with and without chrome oxide. The results indicate that the wear loss in limestone filler blended white Portland cement paste is very high, usually higher than 38 (cm(3) 150 cm(2)). The wear losses of limestone filler blended white Portland cement concretes range from 21.79 to 27.98 (cm(3)/ 50 cm(2)). However, replacement of the limestone filler in the blend by chrome oxide causes a significant decrease in wear loss. This sample has a value of wear loss of 14.83 cm(3) 150 cm(2), which is 6.96 cm(3) 150 cm(2) less than the value found for white Portland cement concrete without chronic oxide. The apparent correlation between wear loss and flexural strength of white Portland cement concrete observed in this study appears significant. (C) 2007 Elsevier Ltd. All rights reserved.