Preparation and characterization of La0.8Sr0.2Ga0.83Mg0.17O3 electrolyte by polyol method for solid oxide fuel cells


Kuguoglu R. S. , Altincekic T. , Ozdemir H. , Oksuzomer M. A. F.

INTERNATIONAL JOURNAL OF HYDROGEN ENERGY, cilt.37, ss.16733-16738, 2012 (SCI İndekslerine Giren Dergi) identifier identifier

  • Cilt numarası: 37 Konu: 21
  • Basım Tarihi: 2012
  • Doi Numarası: 10.1016/j.ijhydene.2012.02.122
  • Dergi Adı: INTERNATIONAL JOURNAL OF HYDROGEN ENERGY
  • Sayfa Sayıları: ss.16733-16738

Özet

Perovskite type La0.8Sr0.2Ga0.83Mg0.17O3 powders were prepared via simple polyol method for the first time in literature. Obtained material was characterized by using XRD, SEM, Impedance Spectroscopy and density measurements. Pure LSGM powders were achieved after heat treatment at 1100 degrees C for 12 h. 87% relative density was obtained after pressing of these powders under 1 MPa and sintering at 1250 degrees C for 12 h. Average particle size was calculated as 1.77-2.4 pal from SEM micrographs. Overall conductivity of the LSGM pellet was found to be 0.0014 S/cm at 850 degrees C with impedance analysis and showed that the preparation process needs improvements. Copyright (C) 2012, Hydrogen Energy Publications, LLC. Published by Elsevier Ltd. All rights reserved.